| 敬兴,黄海洋,骆华英,张敏,董云渊,陈晓彬,陈新志.环保型PLA/CNF应用于纸张阻隔性涂布的研究[J].中国造纸学报,2022,37(3):86-93 |
二维码（扫一下试试看！） |
| 环保型PLA/CNF应用于纸张阻隔性涂布的研究 |
| Study on the Application of Environmental Friendly PLA/CNF in Paper Barrier Coating |
| 投稿时间：2021-12-16 |
| DOI：10.11981/j.issn.1000-6842.2022.03.86 |
| 中文关键词: 可降解 聚乳酸 改性纤维素纳米纤丝 阻隔保鲜纸 |
| Key Words:degradable polylactic acid modified cellulose nanofibrils preservative paper with barrier property |
| 基金项目:国家大学生创新创业项目（202011488034）；浙江省大学生科技创新活动（新苗人才）计划（2020R471011）；浙江大学衢州研究院科技计划项目（IZQ2019-KJ-028）；浙江省重点研发计划项目（2021C02031）；衢州市重点研发计划项目（2021Z01）；衢江区科技计划项目（QJ2019J001、QJ2020012、QJ2020022、QJ2021038）。 |
| 作者 | 单位 | 邮编 | | 敬兴* | 衢州学院化学与材料工程学院,浙江衢州,324000 | 324000 | | 黄海洋 | 衢州学院化学与材料工程学院,浙江衢州,324000 | 324000 | | 骆华英 | 仙鹤股份有限公司,浙江衢州,324000 | 324000 | | 张敏 | 衢州学院化学与材料工程学院,浙江衢州,324000 | 324000 | | 董云渊 | 衢州学院化学与材料工程学院,浙江衢州,324000 | 324000 | | 陈晓彬 | 衢州学院化学与材料工程学院,浙江衢州,324000 | 324000 | | 陈新志 | 浙江大学衢州研究院,浙江衢州,324000 | 324000 |
|
| 摘要点击次数: 2031 |
| 全文下载次数: 1207 |
| 中文摘要: |
| 以聚乳酸（PLA）为基体、乙酰化改性纤维素纳米纤丝（m-CNF）为增强材料制得复合涂料，将其涂覆于A4纸表面制得PLA/m-CNF阻隔纸，探讨了复合涂料中m-CNF添加量对纸张阻隔性能、疏水性能、强度性能等的影响。结果表明，与原纸相比，当m-CNF添加量为3%时，PLA/m-CNF3%阻隔纸的抗张指数、耐破指数、疏水性能分别提高了30.6%、40.1%、24.8%，透气度降低了36.6%。原纸水蒸气透过量为1815 g/（m2·d），PLA/CNF阻隔纸的氧气和水蒸气阻隔性能相较原纸显著提升；其中，PLA/CNF3%阻隔纸的水蒸气透过量为443 g/（m2·d）、氧气透过量为45 cm3/（m2·d·（0.1 MPa））；PLA/m-CNF3%阻隔纸的水蒸气透过量为385 g/（m2·d）、氧气透过量为35 cm3/（m2·d·（0.1 MPa）），与PLA/CNF3%阻隔纸相比，分别下降了13.1%和22.2%；表明PLA/m-CNF阻隔纸具有优异的保鲜效果。 |
| Abstract: |
| Polylactic acid （PLA） as matrix and acetylated modified cellulose nanofibril （m-CNF） as reinforcing material were used to prepare composite coating which was coated on the surface of A4 paper to prepare PLA/m-CNF barrier paper， and effects of additive amount of m-CNF in composite coating on barrier property， hydrophobicity， and strength of the barrier paper were discussed. Compared with base paper， when the additive amount of m-CNF is 3%， the tensile index， burst index， and hydrophobicity of the PLA/m-CNF3% barrier paper increase by 30.6%， 40.1%， and 24.8%， respectively， while the air permeability decreases by 36.6%. The water vapor transmission of base paper is 1815 g/（m2·d） whereas PLA/CNF barrier paper significantly improves the barrier performance on oxygen and water vapor with water vapor transmission of PLA/CNF3% barrier paper of 443 g/（m2·d） and oxygen transmission of 45 cm3/（m2·d·（0.1 MPa））. Compared with PLA/CNF3% barrier paper， the water vapor （385 g/（m2·d）） and oxygen （35 cm3/（m2·d·（0.1 MPa））） transmission of PLA/m-CNF3% barrier paper decreases by 13.1% and 22.2%， respectively， indicating the excellent barrier and preservative performance of the as-prepared PLA/m-CNF barrier paper. |
| 查看全文 查看/发表评论 下载PDF阅读器 HTML |